Artificial Stone Mould Making Silicone Rubber Stone And Tile Concrete Molds
Product Description
Description of Artificial Stone Mould Making Silicone Rubber Stone And Tile Concrete Molds
Silicone rubber MCSIL-2088 is a two-component material, consisting of Part A base silicone and Part B MCSIL-C520, cures at room temperature by a condensation reaction.
Features of Artificial Stone Mould Making Silicone Rubber Stone And Tile Concrete Molds
lGood flow ability and long working time
lMedium hardness
lHigh tear and tensile strength
lEasy de-mould from complex replica parts
lAcid and alkali-resistance
lLow linear shrinkage
TDS of Artificial Stone Mould Making Silicone Rubber Stone And Tile Concrete Molds
| Item No. | Properties before curing | Curing |
| Part A | Part B | Part A+ Part B | Pot life at 250C | De-molding Time at 25℃ |
| Appearance | Appearance | Ratio | Viscosity |
| MCSIL-2088 | White | Clear | 100:2 | 25000±2000 cps | 30-40 mins | 4-6 hours |
| Properties after curing 24 hours |
| Hardness Shore A | Tear strength | Tensile Strength | Elongation break (%) | Linear Shrinkage |
| 32-34 | 28-30 N/mm | 4 ±0.2 Mpa | 450-500 | 0.2-0.4% |
How to make the silicone mold?
- The surface of the original should be clean and free of loose material. If your products with thin flower patterns, and especially with porous substrates, pls use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
- Mixing
Please weight 100 Part A base and 2 parts of B the Curing Agent in a clean container. Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until the CA30 completely dispersed in the base. Hand or mechanical mixing can be used, but do not for an extended period of time or allow the temperature to exceed 35C (95F). Mix suitably small quantities to ensure thorough mixing of base and curing agent.
It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 minutes under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
Pouring the mixture and curing
Pour the mixed Part A base silicone and part B the curing agent as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.
Packaging & Shipping
Artificial Stone Mould Making Silicone Rubber Stone And Tile Concrete Molds
silicone rubber Part A: 1kg=504kg pallet, 5kg/drum=600kg/pallet, 10kg, 20kg per plastic drum=480kg per pallet
200kg per drum, 800kg per pallet. Other types of package, please check with our sales representative.
silicone rubber Part B: 0.8kg/bottle, 1kg/bottle.
Storge of Artificial Stone Mould Making Silicone Rubber Stone And Tile Concrete Molds
When the silicone rubber is stored at or below 30 centi degree in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 10 months from the date of production. After 10 months stockpiles use the Stir to mix the Part A silicone for some minutes, then the silicone can be use again, no influence for other performance.
Certificates
Factory
Related Products
More information of our products, please click below picture
The information above is just for reference, if you're interesting or have any questions, please don't hesitate to contact Sophie.